Arie Wardhono, Chamila Gunasekara, David W. Law, Sujeeva Setunge
This paper reports the comparison of engineering properties of alkali activated slag (AAS) and low calcium fly ash geopolymer (FAGP) concretes up to 540 days. The results showed that the AAS concrete had higher compressive and tensile strength, elastic modulus and lower permeation characteristics than FAGP concrete in the initial 90 days. However, a reduction in AAS concrete performance was observed between 90 and 540 days, while an increase was noted in FAGP concrete over the same time period. The microscopy revealed that both reactions progressed beyond 90 days with the slag–alkali producing excess C–S–H gel which was observed to increase the crack propagation and crack width at latter ages, attributed to the combined effect of disjoining pressure and self-desiccation. The fly ash geopolymerization also continued following an initial 24 h heat curing resulting in a crack-free dense microstructure at 540 days. Overall the discrepancy in microstructural development beyond 90 days in the two concretes would explain the contradictory performance over the longer time frame. © 2017 Elsevier Ltd
Department of Civil Engineering, State University of Surabaya (Universitas Negeri Surabaya), Kampus Unesa Ketintang, Surabaya, 60231, Indonesia; Civil and Infrastructure Engineering, School of Engineering, RMIT University, 124, La Trobe Street, Melbourne, 3000, Victoria, Australia
Research at a Glance
Register to unlock
Topics & SDG Alignment
Register to unlock
Collaboration
Register to unlock
Author Profile (Selected)
Register to unlock
References Overview
Register to unlock
Journal & Source
Register to unlock
Metadata & Integrity
Register to unlock